微量Ce对Cu-Cr-Zr合金性能的影响  

Effect of Trace Ce on Properties of Cu-Cr-Zr Alloy

作　　者：刘勇[1] 刘平[2] 康布熙[2] 田保红[2] 李伟[2] 

机构地区：[1]西安理工大学材料科学与工程学院,陕西西安710048 [2]河南科技大学材料科学与工程学院,河南洛阳471003

出　　处：《稀土》2006年第3期16-19,75,共5页Chinese Rare Earths

基　　金：国家高技术研究发展计划(863)项目(2002AA331110);河南省杰出人才基金项目(0521001200);河南省教育厅自然科学基金项目(2006430004);河南科技大学科研基金资助项目(2004ZY003)

摘　　要：研究了C e对电气化铁路用高强高导接触线Cu-C r-Z r合金的强度、硬度、导电性和耐高温性等的影响。结果表明:微量C e的加入可以提高Cu-C r-Z r合金的强度、硬度和耐热性,抗拉强度可达637M Pa,导电率为82.16%IACS,相对于Cu-C r-Z r合金强度提高了56M Pa,而导电性略有降低。This paer is dealt with the effects of adding trace Ce on the properties （such as strength,hardness,electrical conductivity and heat-resistance, etc. ） of Cu - Cr - Zr contact wire for electrified railway. The results showed that the strength,hardness and heat-resistance of Cu-Cr-Zr alloy were improved,and tensile strength was enhanced from 581 MPa to 637MPa and the electrical conductivity of Cu-Cr-Zr-Ce alloy was 82.16% IACS,which was a bit lower than that of Cu -Cr-Zr-Ce alloy.

关 键 词：高强高导 CU-CR-ZR合金 显微硬度 导电率 

分 类 号：TG146.11[一般工业技术—材料科学与工程] TG132[金属学及工艺—金属材料]