机械合金化制备Fe-Zr-B非晶合金及其晶化动力学行为研究  

Porparation of Fe-Zr-B Amorphous Alloy by Mechanical Alloying and Its Crystallization Behavior

作　　者：吕俊[1] 陈晓虎[1] 陈晓闽[1] 黄东亚[1] 王翠萍[2] 刘兴军[2] 

机构地区：[1]华侨大学材料科学与工程学院,福建泉州362021 [2]厦门大学材料系,福建厦门361005

出　　处：《中国粉体技术》2006年第3期12-15,共4页China Powder Science and Technology

基　　金：福建省科技计划项目;编号20021018;福建省自然科学基金资助项目;编号:E0310021。

摘　　要：在高纯氩气保护下使用机械合金化法对原子组成为Fe60Zr40-xBx(x=10、20、30)的混合粉体进行实验,成功地制取了非晶合金粉。结合X射线衍射与DSC的分析,认为:Fe60Zr20B20和Fe60Zr10B30体系因B原子含量较高,使得其非晶化效率及热稳定性都要高于B原子含量较少的Fe60Zr30B10体系。计算得出Fe60Zr20B20和Fe60Zr10B30两个体系的非晶晶化激活能数据分别为(201.7±58.5)kJ·mol-1和(220.3±18.1)kJ·mol-1。The amorphous alloys of Fe60Zr40-xBx（x =10,20,30, at%） systems were successfully prepared by mechanical alloying under pure argon atmosphere. By X-ray diffraction and differential scanning calorimetry, it was concluded that because of more B atoms the amorphization efficiency and thermo-stability of Fe60Zr20B20 and Fe60Zr10B30 systems were better than Fe60Zr30B10 system. The calculated activation energy of Fe60Zr20B20 and Fe60Zr10B30 were（201.7±58.5） kJ· mol^-1 and （220.3± 18.1） k J·mol^-1 respectively.

关 键 词：机械合金化 非晶合金 晶化动力学 热稳定性 

分 类 号：TB383[一般工业技术—材料科学与工程] TF123.71[冶金工程—粉末冶金]