电刷镀Cu／Ni多层膜的摩擦学性能研究  

Study on the Tribological Properties of Cu/Ni Multilayers Prepared by Brush Plating

作　　者：谭俊[1] 于甜甜[1] 杨红军[1] 徐滨士[1] 郭文才[1] 

机构地区：[1]装甲兵工程学院装备再制造技术国防科技重点实验室,北京100072

出　　处：《装甲兵工程学院学报》2006年第3期77-80,共4页Journal of Academy of Armored Force Engineering

基　　金：国防科技重点实验室基金项目(51489020104JS9102)武器装备预研基金项目(51418060105JB3508)．

摘　　要：采用电刷镀法制备了Cu／Ni多层膜，对多层膜的摩擦学性能进行了研究。结果表明，电刷镀法制备Cu／Ni多层膜镀层平整、均匀致密、晶粒细小，界面清晰；多层膜的摩擦磨损性能直接由单层膜厚决定：随着单层膜厚的减小，多层膜的摩擦系数减小，磨损形式由磨料磨损逐渐转变为粘着磨损；多层膜的磨损量随单层膜厚的减小而减小，当单层膜厚减小至纳米尺度时，存在一磨损量的最小值；电刷镀Cu／Ni多层膜的临界单层膜厚约为20nm。The tribologieal properties of Cu/Ni multilayers prepared by brush plating are investigated. The results show that the multilayers are smooth, dense, small in grain size and elear in interfaee and the tribologieal properties of the multilayers depend on the monolayer thiekness. The frietion eoeffieient of the multilayers decreases with the monolayer thiekness and the wear mechanism ehanges form abrasive to adhesive. The mass loss of the multilayers deereases also with the monolayer thickness and a minimum exists while the thiekness of monolayer deereases to nanoseales. The eritical thiekness of monolayer of the Cu/Ni mulilayes is about 20nm.

关 键 词：电刷镀 纳米多层膜 摩擦学性能 

分 类 号：TG174[金属学及工艺—金属表面处理]