Fe基－Al_2O_3复合材料的界面研究  

A STUDY OF THE INTERFACE IN Fe Al 2O 3 COMPOSITE

作　　者：许承惠[1,2] 吴润[1,2] 田薇 

机构地区：[1]武汉冶金科技大学 [2]北京科技大学

出　　处：《武汉冶金科技大学学报》1996年第3期307-311,共5页

摘　　要：将工业还原铁粉、Ａｌ２Ｏ３颗粒、炭粉及某种适量粘结剂，通过粉末冶金方法在高温下进行烧结，制备了Ａｌ２Ｏ３颗粒增强Ｆｅ基复合材料。用ＳＴＥＭ，ＴＥＭ及ＳＥＭ对界面结合机制进行了分析与研究。结果表明，烧结过程中在Ａｌ２Ｏ３颗粒与Ｆｅ基界面生成了中间相，使Ａｌ２Ｏ３与铁基有良好的结合强度，所制备的Ｆｅ基－Ａｌ２Ｏ３复合材料的硬度。Al 2O 3 particles reinforced metal Fe matrix composite has been prepared at high temperatures by sintering method of powder metallurgy using industrially reduced Fe,Al 2O 3 particles,carbon powders and a kind of binder.Interfacial binding mechanism in the composite was studied and analysed by STEM,TEM and SEM.The results indicated that the formation of intermediate phase at the interface during sintering process resulted in the good binding strength between Al 2O 3 particles and metal Fe matrix.The hardness and abrasive resistance of such prepared composite are superior to those of carbon steel with the same content of carbon.

关 键 词：界面 金属基复合材料 铁 三氧化二铝 粉末 

分 类 号：TF122.1[冶金工程—粉末冶金] TB331[冶金工程—冶金物理化学]