Ti-V-Nb微合金钢第二相粒子研究  

Study on Secondary Phase Particles in Ti-V-Nb Micro Alloyed Steel

作　　者：陈俊华[1] 

机构地区：[1]山东大学材料科学与工程学院材料液态结构及其遗传性教育部重点实验室,济南250061

出　　处：《现代制造技术与装备》2006年第3期12-14,共3页Modern Manufacturing Technology and Equipment

摘　　要：利用萃取复型分析技术,对Ti-V-Nb微合金管线钢中第二相粒子进行了研究。结果表明,钢中存在大量弥散分布的细小粒子,尺寸较大的粒子近似方形,含Ti量较高而含Nb量较低;尺寸较小的粒子形状不规则,含Ti量较低、含Nb量较高;尺寸在20μm以上的粒子中含V量均较低。电子衍射分析表明,粒子具有面心立方结构。这些弥散分布的粒子能够显著阻止奥氏体晶粒长大,在1150℃以下加热时,该钢的奥氏体晶粒长大速度非常小,而在1150℃以上加热时,奥氏体晶粒长大较明显。The secondary phase particles in Ti-V-Nb micro alloyed steel were investigated using carbon extraction-replica technique. The results show there are a large number of fine dispersed particles in the steel. The larger particles like square contain higher Ti and lower Nb. The smaller particles of irregular shape contain lower Ti and Nb. The particles of more than 20 μ m size contain lower V. The electron diffraction analysis shows the particles have face-centered cubic structure. The dispersed particles retard the growth of austenite grains markedly. The austenite grains in the steel heated at below 1150℃ grow at very low speed. The austenite grains in the steel heated at above 1150℃ grow markedly.

关 键 词：第二相粒子 萃取复型 微合金钢 

分 类 号：TG111[金属学及工艺—物理冶金]