EFFECT OF COMPATIBILITY ON PHASE MORPHOLOGY AND ORIENTATION OF ISOTACTIC POLYPROPYLENE (IPP) BLENDS OBTAINED BY DYNAMIC PACKING INJECTION MOLDING  

作　　者：傅强 

机构地区：[1]Department of Polymer Science & Materials, Sichuan University, State Key Laboratory of Polymer Materials Engineering, Chengdu 610065, China

出　　处：《Chinese Journal of Polymer Science》2006年第4期379-387,共9页高分子科学（英文版）

基　　金：This work was financially supported by the National Natural Science Foundation of China (Nos. 20404008, 50373030 and 20490220) the Ministry of Education of China (No. 104154).

摘　　要：The effect of compatibility on phase morphology and orientation of isotactic polypropylene （iPP） blends under shear stress was investigated via dynamic packing injection molding （DPIM）. The compatibility of iPP blended with other polymers, namely, atactic polypropylene （aPP）, octane-ethylene copolymer （POE）, ethylene-propylene-diene rubber （EPDM） and poly（ethylene-co-vinyl acetate） （EVA）, have first been studied using dynamic mechanical analysis （DMA）. These blends were subjected to DPIM, which relies on the application of shear stress fields to the melt/solid interfaces during the packing stage by means of hydraulically actuated pistons. The phase morphology, orientation and mechanical properties of the injection-molded samples were characterized by SEM, 2D WAXS and Instron. For incompatible iPP/EVA blends, a much elongated and deformed EVA particles and a higher degree of iPP chain orientation were observed under the effect of shear. However, for compatible iPP/aPP blends, a less deformed and elongated aPP particles and less oriented iPP chains were deduced. It can be concluded that the compatibility between the components decreases the deformation and orientation in the polymer blends. This is most likely due to the hindering effect, resulting from the molecular entanglement and interaction in the compatible system.The effect of compatibility on phase morphology and orientation of isotactic polypropylene （iPP） blends under shear stress was investigated via dynamic packing injection molding （DPIM）. The compatibility of iPP blended with other polymers, namely, atactic polypropylene （aPP）, octane-ethylene copolymer （POE）, ethylene-propylene-diene rubber （EPDM） and poly（ethylene-co-vinyl acetate） （EVA）, have first been studied using dynamic mechanical analysis （DMA）. These blends were subjected to DPIM, which relies on the application of shear stress fields to the melt/solid interfaces during the packing stage by means of hydraulically actuated pistons. The phase morphology, orientation and mechanical properties of the injection-molded samples were characterized by SEM, 2D WAXS and Instron. For incompatible iPP/EVA blends, a much elongated and deformed EVA particles and a higher degree of iPP chain orientation were observed under the effect of shear. However, for compatible iPP/aPP blends, a less deformed and elongated aPP particles and less oriented iPP chains were deduced. It can be concluded that the compatibility between the components decreases the deformation and orientation in the polymer blends. This is most likely due to the hindering effect, resulting from the molecular entanglement and interaction in the compatible system.

关 键 词：Compatibility Phase morphology ORIENTATION Stress. 

分 类 号：TQ320.1[化学工程—合成树脂塑料工业]