BRITTLE-DUCTILE TRANSITION OF PP/EPDM/ELASTOMERIC NANO-PARTICLE TERNARY BLENDS  

作　　者：傅强 

机构地区：[1]Department of Polymer Science and Materials, Sichuan University, State Key Laboratory of Polymer Materials Engineering, Chengdu 610065, China

出　　处：《Chinese Journal of Polymer Science》2006年第4期389-394,共6页高分子科学（英文版）

基　　金：This work was financially supported by the National Natural Science Foundation of China (Nos. 20404008, 50373030 and 20490220) the Special Funds for Major State Basic Research Projects of China (No. 2003CB615600) the Ministry of Education of China as a Key Project (No. 104154).

摘　　要：The brittle-ductile transition is a very important phenomenon for polymer toughening. Polypropylene （PP） is often toughened by using rubbers, e.g., ethylene-propylene diene monomer （EPDM） has often been used as a modifier. In this article, the toughening of PP by using a new kind of rubber, known as elastomeric nano-particle （ENP）, and the brittleductile transition of PP/EPDM/ENP was studied. Compared to PP/EPDM binary blends, the brittle-ductile transition of PP/EPDM/ENP ternary blends occurred at lower EPDM contents. SEM experiment was carried out to investigate the etched and impact-fractured surfaces. ENP alone had no effect on the impact strength of PP, however, with the same EPDM content, PP/EPDM/ENP ternary blends had smaller particle size, better dispersion and smaller interparticle distance in contrary to PP/EPDM binary blends, which promoted the brittle-ductile transition to occur earlier.The brittle-ductile transition is a very important phenomenon for polymer toughening. Polypropylene （PP） is often toughened by using rubbers, e.g., ethylene-propylene diene monomer （EPDM） has often been used as a modifier. In this article, the toughening of PP by using a new kind of rubber, known as elastomeric nano-particle （ENP）, and the brittleductile transition of PP/EPDM/ENP was studied. Compared to PP/EPDM binary blends, the brittle-ductile transition of PP/EPDM/ENP ternary blends occurred at lower EPDM contents. SEM experiment was carried out to investigate the etched and impact-fractured surfaces. ENP alone had no effect on the impact strength of PP, however, with the same EPDM content, PP/EPDM/ENP ternary blends had smaller particle size, better dispersion and smaller interparticle distance in contrary to PP/EPDM binary blends, which promoted the brittle-ductile transition to occur earlier.

关 键 词：PP EPDM Elastomeric nano-particle Brittle-ductile transition. 