非稳态浇铸时IF钢铸坯表层夹杂物粒径的分布  

Distribution of Inclusion Size in Surface Layer of IF Steel Slab under Unsteady Casting

作　　者：张乔英[1] 王立涛[2] 王新华[1] 王万军[1] 李宏[1] 

机构地区：[1]北京科技大学冶金与生态学院,北京100083 [2]首钢技术研究院,北京100043

出　　处：《特殊钢》2006年第5期9-11,共3页Special Steel

摘　　要：用原位统计分布分析仪(OPA-100)研究了拉速变化时(1.4 m/m in至0.6 m/m in,0.6 m/m in至1.4 m/m in)IF钢1 150 mm×230 mm铸坯表层试样夹杂物粒径和频数的分布。结果表明,夹杂物粒径与其频数分布规律基本符合一阶指数衰减曲线,夹杂物粒径x(μm)与频数y的拟合公式为y=A1.exp(-x/t1)+y0;式中A1,t1,y0为常数;R为相关系数(R2>0.97)。The distribution of size and frequency of inclusion in samples of surface layer of IF steel 1 150 mm × 230 mm casting slab with unsteady casting speed （ 1.4 m/min to 0.6 m/min and 0.6 m/min to 1.4 m/min） has been studied by Original Position Analysis System （OPA-100）. The results show that the distribution nile of size and frequency of inclusion basically accords with first-order exponential decay curves. The expressions of inclusion size x （μm） and frequency y is y - A1 · exp （ - x/t1 ） ＋ y0 ; A1, t1 and y0 are constant, R is related coefficient （ R^2 〉 0.97）.

关 键 词：非稳态浇铸 板坯 原位分析仪 夹杂物粒径 分布 

分 类 号：TF777[冶金工程—钢铁冶金]