超重力法制备纳米Y型酞菁氧钛  

Preparation of Nano Sized Y-Type Oxytitanium Phthalocyanine Using High Gravity Technology

作　　者：卞曙光[1] 余银霞[1] 陈建峰[1] 

机构地区：[1]纳米材料先进制备技术与应用科学教育部重点实验室,北京化工大学北京100029

出　　处：《化学反应工程与工艺》2006年第3期235-239,共5页Chemical Reaction Engineering and Technology

基　　金：863计划(2004AA302010);教育部重大项目(305002)

摘　　要：采用超重力旋转填充床制备了纳米 Y 型酞菁氧钛(Y-TiOPc),并与烧瓶中的研究结果进行了比较。结果表明,在旋转填充床中可以得到粒径为55 nm 左右的 Y-TiOPc,其饱和电位为-538 V,半衰曝光量为0.452 lux·s,在波长200～450 nm 和550～850 nm 内具有良好的吸收,相对于传统方法制备的 Y-TiOPc 具有明显的光导性能优势,可以满足办公室自动化的应用需要。Nano sized Y-type oxytitanium phthalocyanine （Y-TiOPc） was prepared in a high gravity rotating packed bed （RPB） or flasks. Experimental results indicated that Y-TiOPc prepared in RPB had a particle size of about 55 nm, charging potential of -538 V and energy for half-discharge of potential of 0. 452 lux·s. The prepared Y-TiOPc has excellent absorption performance in the wavelength of 200-450 nm and 550- 850 nm and can meet the requirements of office automation due to obvious advantages over conventional methods.

关 键 词：纳米酞菁氧钛 超重力旋转填充床 光导性能 

分 类 号：TQ132[化学工程—无机化工]