Phase diagrams of Li_2MoO_4-Na_2MoO_4 and Na_2MoO_4-K_2MoO_4 systems  

作　　者：DING Yimin HOU Na CHEN Nianyi XIA Yiben 

机构地区：[1]College of Sciences, Shanghai University, Shanghai 200444, China [2]School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China

出　　处：《Rare Metals》2006年第4期316-320,共5页稀有金属（英文版）

基　　金：This work was financially supported by the National Natural Science Foundation of China (No.20373040).

摘　　要：The phase diagrams of the Li2MoO4-Na2MoO4 and Na2MoO4-K2MoO4 systems have been reassessed using differential thermal analysis together with high-temperature and room-temperature X-ray diffraction analysis. The results showed that the compound Li2MoO4.6Na2MoO4 did not exist; however, it confirmed the existence of the compound Li2MoO4.3Na2MoO4 in the Li2MoO4-Na2MoO4 systen＇ls. With regard to the system of Na2MoO4-K2MoO4, we could not confirm the results reported by Bukhanova who claimed that the system was eutectic type with 1：1 and 1：2 intermediate compounds, refuting the statement of Amadori who thought there was an apparent phase boundary at high temperature in α-solid solution region of the Na2MoO4-K2MoO4 binary system. The revised phase diagrams of these systems are illustrated in this article. These experimental results are in agreement with the computerized prediction using the support vector machine-atomic parameter method for the assessment of phase diagrams.The phase diagrams of the Li2MoO4-Na2MoO4 and Na2MoO4-K2MoO4 systems have been reassessed using differential thermal analysis together with high-temperature and room-temperature X-ray diffraction analysis. The results showed that the compound Li2MoO4.6Na2MoO4 did not exist; however, it confirmed the existence of the compound Li2MoO4.3Na2MoO4 in the Li2MoO4-Na2MoO4 systen＇ls. With regard to the system of Na2MoO4-K2MoO4, we could not confirm the results reported by Bukhanova who claimed that the system was eutectic type with 1：1 and 1：2 intermediate compounds, refuting the statement of Amadori who thought there was an apparent phase boundary at high temperature in α-solid solution region of the Na2MoO4-K2MoO4 binary system. The revised phase diagrams of these systems are illustrated in this article. These experimental results are in agreement with the computerized prediction using the support vector machine-atomic parameter method for the assessment of phase diagrams.

关 键 词：phase diagram DTA Li2MoO4 Na2MoO4 K2MoO4 

分 类 号：O614.11[理学—无机化学]