MoS_2-Ti复合膜的结构及其抗氧化性能  

The Structure and Anti-Oxidation Property of MoS_2-Ti Composite Film

作　　者：胡志彪[1] 李贺军[1] 付前刚[1] 文晓斌[2] 孙国岭[1] 黄凤萍[1] 

机构地区：[1]西北工业大学超高温复合材料重点实验室碳/碳复合材料工程技术研究中心,陕西西安710072 [2]西安理工大学材料科学与工程系,陕西西安710068

出　　处：《稀有金属材料与工程》2006年第A02期216-219,共4页Rare Metal Materials and Engineering

基　　金：国家杰出青年基金(50225210);航空科学基金(03H53044);西北工业大学博士论文创新基金资助

摘　　要：利用非平衡磁控溅射仪在碳／碳复合材料表面制备了MoS2-Ti复合膜。采用XRD,Raman光谱、X射线光电子能谱仪对其结构进行了表征,并利用X射线光电子能谱仪对复合膜的抗氧化性能进行了研究。研究结果表明:所制备的MoS2-Ti复合膜为非晶态结构;MoS2-Ti复合膜具有良好的抗氧化性能,将其在蒸馏水中浸泡200 h后,Mo4+没有被氧化。The MoS2-Ti composite films were prepared by unbalance magnetic sputter technique. The structure of composite film was characterized by XRD, Raman spectroscopy, XPS. The anti-oxidation property of the composite film was studied. The results show that the structure of carbon film is amorphous. The composite films show good anti-oxidation properties, and Mo^4＋ was not oxidized after the composite films were immersed in the distilled water for 200 h.