Y_2O_3:Eu^(3+)氧化物的制备与结构及其发光性能  

Synthesis、Structure and Spectrum Properties of Red Phosphor Y_2O_3:Eu^(3+) Oxide

作　　者：屈芸[1] 孙曰圣[2] 卢爱军[1] 罗赛珍[1] 金明[1] 

机构地区：[1]南昌大学理学院,江西南昌330029 [2]南昌大学环工学院,江西南昌330029

出　　处：《南昌大学学报（理科版）》2006年第4期372-374,378,共4页Journal of Nanchang University(Natural Science)

摘　　要：对用草酸沉淀法制备的、不经球磨的红色发光材料Y2O3:Eu3+的结构和发光性能进行了研究。结果表明:该荧光粉大小分布均匀,一次粒径为4~6μm,最大激发峰位于238 nm,最大发射峰位于613 nm,荧光粉色品坐标x=0.645 4,y=0.340 8,相对亮度为181,可满足灯用荧光粉的要求。The Structure and Spectrum Properties of non-balled red phosphor Y2O3： Eu^3＋ synthesized by oxalic acid precipitation method were carried out in this experiment. The result shows that the size of the phosphor has a good homogeneity. The phosphor is fine and uniformly distributed. The diameter of the phosphor is 4-6 μm. The maximum peaks of excitation spectrum （λex） of the phosphor is at 238 nm. , the maximum peaks of emission spec- trum （~.em） is at 613 nm. ,the luminescent chromatic coordinate parameters are x = 0. 645 4,y = 0.340 8 and the relative luminescent is 181. The red phosphor meets with the demand of application as lamp phosphor.

关 键 词：发光材料 Y2O3:Eu^3+ 结构 发光性能 

分 类 号：TF123[冶金工程—粉末冶金]