硅酸铝质喷补料烧后线变化及其影响因素  

Investigation on linear change after baking or aluminosilicate gunning mix

作　　者：王习东[1] 郑越[1] 李洪泉 

机构地区：[1]华东冶金学院

出　　处：《耐火材料》1996年第6期337-339,共3页Refractories

摘　　要：在以焦宝石、矾上熟料为基本骨料，以高铝水泥等为复合结合剂的喷补料中加入３％的Ａｌ２Ｏ３超细粉或５％的蓝晶石粉都有利于降低喷补层的烧后线变化。而且加入３％的Ａｌ２Ｏ３超细粉还有利于提高喷补料的附着率及喷补层与受补体间的粘结强度。通过在轧钢加热炉上的喷补实践，较大地延长了加热炉的使用寿命。Linear change after baking of the gunning mix which takes clay and bauxite as aggregates and high alumina cement as binder can be obviously reduced by adding 30% alumina fine powder and 5% kyanite.Rebound rate and bond strength can also be improved by adding 3% alumina fine powder.The service life of the reheating furnace has been prolonged when it was used.

关 键 词：喷补料 硅酸铝质 烧后线变化 烧成 耐炎材料 

分 类 号：TQ175.733[化学工程—硅酸盐工业]