A Comparative Study on the Pozzolanic Activity between Nano-SiO_2 and Silica Fume  

作　　者：叶青 

机构地区：[1]College of Civil Engineering, Zhejiang University of Technology, Hangzhou 310014,China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2006年第3期153-157,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded bythe Center of Science Research, Zhejiang Universityof Technology of China

摘　　要：The pozzolanic activity of nano-SiO2 and silica fume was comparatirely stndied by X-ray diffraction （ XRD ） , differential scanning calorimetry （DSC）, scanning electron micrascopy （SEM） and the compressive , bond and bending streugths of hardened paste and concrete were also measured. Results indicate that the compressive strength development of the paste made from Ca（OH）2 and nano-SiO2, the reaction rate of Ca（ OH）2 with nano- SiO2 and the velocity of C-S-H gel formation from Ca （ OH）2 with nano-SiO2 showed marked increases over those of Ca（ OH）2 with silica fume. Furthermore, the bond strength at the interface between aggregate and hardened cement paste, and the bending strength of concrete incorporated with 3% .NS increased more than those with SF, especially at early ages. To sum up, the pozzolanic activity of nano-SiO2 was much greater than that of silica fume. The results suggest that with a small amount of nano-SiO2, the Ca（ OH）2 crystal at the interface between hardened cement paste and aggregate at early ages may be effectively absorbed in high performance concrete.The pozzolanic activity of nano-SiO2 and silica fume was comparatirely stndied by X-ray diffraction （ XRD ） , differential scanning calorimetry （DSC）, scanning electron micrascopy （SEM） and the compressive , bond and bending streugths of hardened paste and concrete were also measured. Results indicate that the compressive strength development of the paste made from Ca（OH）2 and nano-SiO2, the reaction rate of Ca（ OH）2 with nano- SiO2 and the velocity of C-S-H gel formation from Ca （ OH）2 with nano-SiO2 showed marked increases over those of Ca（ OH）2 with silica fume. Furthermore, the bond strength at the interface between aggregate and hardened cement paste, and the bending strength of concrete incorporated with 3% .NS increased more than those with SF, especially at early ages. To sum up, the pozzolanic activity of nano-SiO2 was much greater than that of silica fume. The results suggest that with a small amount of nano-SiO2, the Ca（ OH）2 crystal at the interface between hardened cement paste and aggregate at early ages may be effectively absorbed in high performance concrete.

关 键 词：Ca（OH）2 INTERACTION NANO-SIO2 pozzolanic activity silica fume 

分 类 号：TB383.1[一般工业技术—材料科学与工程]