高密度聚乙烯/纳米辉钼矿复合材料性能研究  

STUDY ON THE PROPERTIES OF HIGH-DENSITY POLYETHYLENE FILLED WITH NANO-MOLYBDENITE

作　　者：吴伟端[1] 周丽春[1] 郭胜平[1] 牛牧童[1] 肖凤英[1] 赵煌[1] 

机构地区：[1]华侨大学材料科学与工程学院,福建泉州362011

出　　处：《矿物学报》2006年第3期281-284,共4页Acta Mineralogica Sinica

基　　金：华侨大学研究生专项经费

摘　　要：以径厚为30—45nm的辉钼矿作为导电填料，采用熔融共混法制备高密度聚乙烯／纳米辉钼矿复合材料，应用高阻计ZC-36、SEM、XRD、TC．等研究复合材料的电性能、晶体结构、界面微观形貌、热性能等。研究结果表明：当纳米辉钼矿含量为25％，复合材料的体积电阻率为5．1×10^9Ωcm，纳米辉铝矿高定向排列，呈链状集合体；复合材料tonset分解温度提高了35℃；辉钼矿的晶体结构发生变化，（002）晶面2θ右移了1．12°，面间距缩小0．257nm.The composites were prepared by melt-mixing high-density polyethylene filled with nano-molybdenite. The electrical resistivity, crystal structure, microstructure and thermal properties of the composites were studied by using ZC- 36, SEM, XRD, DSC and TG. The results showed that when the composite was filled with 25% nano-molybdenite, the electrical resistivity was 5.1 × 10^9 Ω· cm , the temperature for tonset to decompose increased by 35 ℃ and the diffraction peak of （002） in molybdenite shiftted by 1.12 degrees to the right with 0.257 nm diminution of grating space.

关 键 词：纳米辉钼矿 高密度聚乙烯 晶体结构 电性能 热性能 

分 类 号：P579[天文地球—矿物学] TB332[天文地球—地质学]