快干硅溶胶型壳的胶凝快干机理探讨  

Investigation on the Coagulation Quick Drying Mechanism of the Quick-dry Silica Sol Shell

作　　者：袁新强[1] 曾明[1] 徐道芬[1] 

机构地区：[1]西华大学材料科学与工程学院,四川成都610039

出　　处：《铸造》2006年第10期1088-1090,共3页Foundry

摘　　要：采用室温胶态成型技术制备硅溶胶型壳,所用原料有FS-Ⅱ快干硅溶胶、JN-30硅溶胶和石英粉。实验研究发现:控制环境温度(22±2)℃、相对湿度50%～60%和风速4～6 m/s时,FS-Ⅱ型快干硅溶胶型壳的胶凝硬化时间为3 h,而JN-30硅溶胶型壳为12 h。并通过硅溶胶和快干硅溶胶的结构与稳定性比较,探讨了快干硅溶胶型壳的胶凝快干机理。The silica sol shell was obtained by using colloidal processing technique at room temperature. The initial used to prepare silica sol shell were the FS- Ⅱ quick-dry silica sol, JN-30 silica sol and silica powder. There are three control experimental conditions, ambient temperature 22±2 ℃, relative humidity 50%-60% and wind velocity 4-6 m/s. It is found that the coagulation harden time of the FS- Ⅱ quick-dry silica sol shell is 3 h; the JN-30 silica sol shell is 12 h. The coagulation quick drying mechanism of the quick-dry silica sol shell was investigated by comparison with the stability and structure for the silica sol and auick-drv silica sol.

关 键 词：快干硅溶胶 稳定性 胶凝 硬化时间 

分 类 号：TG223[金属学及工艺—铸造]