铝合金室内加速腐蚀与大气暴露腐蚀的相关性  

Investigation on interrelation of indoor accelerated corrosion testing and atmospheric exposure testing of LY12 alloy

作　　者：郝美丽[1] 曹学军[1] 封先河[2] 史秀梅[1] 方晓祖[1] 

机构地区：[1]中国兵器科学研究院宁波分院,浙江宁波315103 [2]中国兵器工业集团第五九研究所,重庆400041

出　　处：《兵器材料科学与工程》2006年第5期28-31,共4页Ordnance Material Science and Engineering

基　　金：国防科技工业技术基础项目(H092001D002)

摘　　要：通过对LY12铝合金进行实验室盐雾、湿热、干燥以及浸渍的循环复合加速腐蚀试验,对比研究了(NH4)2SO4、NaHSO3、(NH4)2SO4和NaHSO3浸渍溶液对LY12铝合金腐蚀的影响。探索与海南万宁试验站LY12铝合金材料的环境试验腐蚀规律相近的加速模拟试验方法,进行相关性分析。分析结果表明,浸渍溶液为10-2 mol/L NaHSO3(pH约为5.47)的加速试验结果与环境试验腐蚀规律相近。The accelerated corrosion simulation test of LY12 alloy was carried out. The samples were salt sprayed,wet-heated, dried and then dipped in（NH4）2SO4, NariSO3, （NH4）2SO4 and NariSO3 solution separately. The analytical results indicated that the testing method of dipping in NariSO3 solution was the most similar to the environment testing corrosion of LY12 alloy obtained from Hainai Wanning testing station.The interrelation study was carried out.

关 键 词：LY12铝合金 加速腐蚀试验 大气暴露试验 相关性分析 腐蚀规律 

分 类 号：TG172[金属学及工艺—金属表面处理]