FeAl系电热爆炸等离子体喷涂层高温耐蚀性能研究  

Research of Anti-corrosion and Heat Resistance Performance of Electro-thermal Explosion Plasma Spray Coating of FeAl Base

作　　者：魏世丞[1] 徐滨士[1] 王海斗[1] 金国 吕红[1] 

机构地区：[1]装备再制造技术国防科技重点实验室,北京100072

出　　处：《中国表面工程》2006年第5期1-5,21,共6页China Surface Engineering

基　　金：国家863计划项目(2003AA331130)

摘　　要：利用金属导体FeAl系合金箔,电热爆炸产生的瞬间高能量冲击波效应,制备FeAl、FeCrAl、FeCrAlRE等离子体喷涂层。通过涂层SEM等检测,可以看出涂层致密,同时涂层与基体可以形成冶金结合层,涂层与基体之间存在明显的过渡层。经高温氧化、氯化、硫化耐蚀性测试,得出3种等离子体喷涂层的腐蚀变化规律,从而优选出耐高温腐蚀的FeCrAlRE电热爆炸等离子体涂层。Three kinds of plasma spray coatings FeA1, FeCrA1 and FeCrA1RE were prepared using instantaneous high-energy shock wave effect during electro-thermal explosion of FeA1 conductor alloy foil. It was shown that the spray coatings possess mixed nano- and micro-structures, they can form a metallurgical bonding with substrate and an evident buffer layer between coating and base metal. The corrosion rule of these three plasma spray coatings can be obtained through anti-corrosion testes under the conditions of high temperature oxidation, chloridization, and sulfuration, and then The FeCrA1RE electro-thermal explosion plasma spray coating was selected for anti-corrosion and heat resistance use.

关 键 词：电热爆炸 等离子体喷涂层 FeCrAlRE 耐高温腐蚀 

分 类 号：TG174.2[金属学及工艺—金属表面处理]