微波法制备立方相BaTiO_3及其表征  

Preparation and Characterization of Cubic Phase Barium Titanate by Microwave Method

作　　者：李军平[1] 畅功民[2] 郑娜[1] 张智敏[1] 

机构地区：[1]山西大学化学化工学院,山西太原030006 [2]山西省农业科学院,山西太原030031

出　　处：《山西大学学报（自然科学版）》2006年第4期388-390,共3页Journal of Shanxi University(Natural Science Edition)

基　　金：山西省教育厅高校科技研究开发项目

摘　　要：采用微波法制备了纳米晶B aT iO3,并通过XRD、SEM、TG及原子吸收等对产物进行了表征.XRD分析表明晶体为立方相B aT iO3,SEM显示B aT iO3颗粒形貌主要为立方相,一次粒子的粒径约为50 nm,TG分析表明所制得的B aT iO3粉体晶形稳定,原子吸收分析表明所制得的B aT iO3粉体杂质总含量为0.0261%.The nano-crystalline Barium Titanate was prepared by the microwave method. The morphological feature of the product was characterized by ways of XRD, SEM, TG and atomic absorption. The result showed that the crystal was cubic phase structure by XRD analysis and the first grade grain size was about 50 nm by SEM ;the crystal form was stable using TG;the amount of impurity was about the percent of 0. 0261 by the atomic absorption.

关 键 词：立方相 BATIO3 微波法 纳米晶 

分 类 号：TB383[一般工业技术—材料科学与工程]