Al-F复合改性LiMn_2O_4的结构和性能  

Study on the synthesis and characterization of Al-F multiplex modified LiMn_2O_4

作　　者：蔡振平[1] 金维华[1] 李明勋[1] 

机构地区：[1]北京有色金属研究总院,北京100088

出　　处：《功能材料》2006年第11期1737-1738,1742,共3页Journal of Functional Materials

基　　金：国家自然科学基金(50472088)

摘　　要：通过固态反应制备了尖晶石型锂锰氧化物LiAl_(0．2)Mn_(1．8)O_(4-x)F_x锂离子电池正极材料,采用XRD、EDS等测试对其进行了表征,并测试了样品的电化学性能。结果表明,合成的LiAl_(0．2)Mn_(1．8)O_(4-x)F_x(0≤x≤0．3)样品为单一的尖晶石结构；随着F^-含量的增加,晶胞参数增大；一定量的Al^(3+)和F^-复合改性提高了材料的比容量,增加了尖晶石结构的稳定性,改善了材料的高温循环性能。The modified spinel lithium-manganese oxygen LiAl0.2Mn1.8O4-xFx as cathode material for ion battery was synthesized by solid state reaction. The crystal structure and electrochemical performance of the samples were studied by XRD, EDS and charge-discharge tests. Results showed that the samples of LiAl0.2Mn1.8O4-xFx （0≤x≤0.3） possessed pure spinel phase. With the content of F^- increasing, the lattice parameters increased. The special capacity of the material was increased, the stability of spinel structure and elevated temperature cycle performance were improved by a content of Al^3＋ and F^- multiplex modifying.

关 键 词：锂离子电池 尖晶石LIMN2O4 复合改性 

分 类 号：TM912.9[电气工程—电力电子与电力传动]