TiO_2的含量对铁基合金激光熔覆层组织和性能的影响  

Microstructure and properties of laser cladding layers of Fe-based alloy doped with TiO_2 of different percentages

作　　者：余菊美[1] 晁明举[2] 卢洵[1] 梁二军[2] 

机构地区：[1]解放军信息工程大学理学院数理系,郑州450001 [2]郑州大学物理工程学院教育部材料物理重点实验室,郑州450052

出　　处：《激光杂志》2006年第6期70-71,共2页Laser Journal

基　　金：河南省高校创新人才基金(1999-125);河南省杰出人才基金(0121001200)资助

摘　　要：在45#钢基底上进行了铁基合金粉末G312和铁基合金粉末G312中加入不同百分比的TiO2的激光熔覆实验。借助裂纹检测、金相显微镜、扫描电镜、x射线衍射、硬度测试、摩擦磨损实验等手段,发现:随着加入的TiO2的含量的增加,熔覆层组织结构和组成成分也呈现明显的不同。在一定的工艺条件下,加入适量的TiO2可以提高G312熔覆层的硬度、耐磨性、降低开裂敏感性,改善熔覆层的综合性能。The laser cladding of Fe - based alloy of various percent TiO2 on steel 45 by powder feeding were carried. The experiments of cracks check,microstructure observation , X - ray diffractien, the hardness measurements and the wear resistance tests showed that the microstructure and properties of layers were different when the percentage of TiO2 changed. The result is that adding suitable amount of TiO2 to Fe - based alloy can improve the hardness, wear resistance and reduce the cracking susceptibility of coatings.

关 键 词：激光熔覆 铁基合金 TIO2 含量 裂纹 组织 耐磨性 

分 类 号：TN248.1[电子电信—物理电子学]