LaFe_(11.17-x)Co_(0.78)Si_(1.05)B_x合金磁热效应的研究  

The magnetocaloric effect in LaFe_(11.17-x)Co_(0.78)Si_(1.05)B_x alloys

作　　者：黄焦宏[1] 松林[2] 金培育[3] 王高峰[2] 刘金荣[3] 闫宏伟[3] 张久兴[1] 

机构地区：[1]北京工业大学新型功能材料教育部重点实验室,北京100022 [2]内蒙古师范大学磁性材料重点实验室,内蒙古呼和浩特010022 [3]包头稀土研究院,内蒙古包头014010

出　　处：《功能材料》2006年第12期1888-1890,共3页Journal of Functional Materials

摘　　要：用工业纯原料研究了LaFe11.17-xCo0.78Si1.05Bx(x=0、0.1、0.2、0.3、0.4、0.5)合金在室温附近的磁热效应。B元素作为间隙原子进入晶胞,随着B含量的增加,磁相变点从x=0时的277K升高到x=0.3时的289K。同时,磁熵变和直接测量的绝热温变也随着B含量的增加而增大了,在低磁场具有较大的磁热效应。测量表明合金的热滞和磁滞均很小。The have studied the magnetocaloric effect around room temperature of LaFe11.17-xCo0.78Si1.05Bx （x=0, 0.1,0.2,0. 3,）alloys using commercial pure material. The element B is interstitial atom. The phase transition temperature increase from 277K for x=0 to 289K for x=0.3 with increasing B content. Simultaneity,the magnetic entropy change and adiabatic temperature change which measured directly also increase as increasing B content,and show large magnetocaloric effect at lower magnetic field. Measurements also indicate that both thermal hysteresis and hysteresis are rather small.

关 键 词：磁热效应 磁相变温度 工业纯 B元素 

分 类 号：TM271.4[一般工业技术—材料科学与工程]