含磷聚醚醚酮酮砜的合成与表征  

SYNTHESIS AND CHARACTERIZATION OF A PHOSPHORUS-CONTAINING POLY(ETHER ETHER KETONE KETONE SULFONE)

作　　者：孙皓[1] 陈晓婷[1] 唐旭东[1] 王春颖[1] 

机构地区：[1]天津科技大学材料科学与化学工程学院,天津300222

出　　处：《高分子学报》2007年第1期90-92,共3页Acta Polymerica Sinica

基　　金：国家自然科学基金(基金号50203008)资助项目

摘　　要：A new kind of phosphorus-containing monomer bis（4-（p-fluorobenzoyl）phenyl）phenylphosphine oxide was synthesized first,then a poly（aryl ether ketone） containing phosphorus in the main ring was synthesized,derived from bis（4-（p-fluorobenzoyl）phenyl）phenylphosphine oxide and bisphenol-S by nucleophilic copolycondensation with the use of sulfolane as solvent.The structure was confirmed by FT-IR,（）31P-NMR and（）1H-NMR.Electrical property,mechanical property,heat-resistance property,combustion-resistance and solubility was also researched to know the influence of the containing of phosphorus.The results showed that the polymer have excellent heat-resistance,the glass transition temperature（Tg） was 235℃.The onset temperature taken at 5% weight loss of the polymer in nitrogen was 463℃.The polymer was soluble in CH2Cl2,CHCl3,Cl2（CH）2Cl2,Cl（CH2）2Cl and strongly polar organic solvents such as（N,N-dimethylformamide）（DMF）,N-methyl2pyrrolidone （NMP） at room temperature.A new kind of phosphorus-containing monomer bis （4- （p-fluombenzoyl） phenyl）phenylphosphine oxide was synthesized first,then a poly（aryl ether ketone） containing phosphorus in the main ring was synthesized,derived from his （4-（p-fluorobenzoyl） phenyl）phenylphosphine oxide and bisphenol-S by nucleophilic copolycondensation with the use of sulfolane as solvent. The structure was confirmed by FT-IR, 31 P-NMR and ^1H-NMR. Electrical property, mechanical property, heat-resistance property, combustion-resistance and solubility was also researched to know the influence of the containing of phosphorus. The results showed that the polymer have excellent heatresistance, the glass transition temperature （ Tg ） was 235℃. The onset temperature taken at 5 % weight loss of the polymer in nitrogen was 463 ℃. The polymer was soluble in CH2 Cl2, CHCl3, Cl2 （ CH）2 Cl2, Cl（ CH2 ）2 Cl and strongly polar organic solvents such as N, N-dimethylformamide （.DMF）, N-methyl-2-pyrrolidone （NMP） at room temperature.

关 键 词：聚芳醚酮 含磷单体 双(4-(对氟苯甲酰基)苯基)苯基氧化膦 亲核取代 

分 类 号：TQ326.5[化学工程—合成树脂塑料工业]