SPATIAL HIERARCHY AND INTERFACIAL STRUCTURE IN INJECTION-MOLDED BARS OF POLYPROPYLENE-BASED BLENDS AND COMPOSITES  

作　　者：傅强 

机构地区：[1]Department of Polymer Science and Materials,Sichuan University,State Key Laboratory of Polymer Materials Engineering

出　　处：《Chinese Journal of Polymer Science》2007年第1期23-33,共11页高分子科学（英文版）

基　　金：This work was supported by the National Natural Science Foundation of China (Nos. 20404008, 50533050, 50373030 and 20490220). This work is subsidized by the Special Funds for Major State Basic Research Projects of China (No. 2003CB615600) by Ministry of Education of China as a key project (No. 104154).

摘　　要：The hierarchical structure and interfacial morphology of injection-molded bars of polypropylene （PP） based blends and composites have been investigated in detail from the skin to the core. For preparation of injection-molded bars with high-level orientation and good interfacial adhesion, a dynamic packing injection molding technology was applied to exert oscillatory shear on the melts during solidification stage. Depending on incorporated component, interfacial adhesion and processing conditions, various oriented structure and morphology could be obtained. First, we will elucidate the epitaxial behavior between PP and high-density polyethylene occurring in practical molded processing. Then, the shear-induced transcrystalline structure will be the main focus for PP/fiber composites. At last, various oriented clay structures have been ascertained unambiguously in PP/organoclay nanocomposites along the thickness of molded bars.The hierarchical structure and interfacial morphology of injection-molded bars of polypropylene （PP） based blends and composites have been investigated in detail from the skin to the core. For preparation of injection-molded bars with high-level orientation and good interfacial adhesion, a dynamic packing injection molding technology was applied to exert oscillatory shear on the melts during solidification stage. Depending on incorporated component, interfacial adhesion and processing conditions, various oriented structure and morphology could be obtained. First, we will elucidate the epitaxial behavior between PP and high-density polyethylene occurring in practical molded processing. Then, the shear-induced transcrystalline structure will be the main focus for PP/fiber composites. At last, various oriented clay structures have been ascertained unambiguously in PP/organoclay nanocomposites along the thickness of molded bars.

关 键 词：POLYPROPYLENE Injection-molded bar Interfacial structure Orientation TRANSCRYSTALLIZATION Blend and composite. 

分 类 号：O632.12[理学—高分子化学]