铁基纳米非晶丝脉冲电流退火的最佳电流密度研究  

Study on optimal current density to annealing Fe-based amorphous wire by pulse current

作　　者：杨晓红[1] 郑金菊[2] 方允樟[2] 任俊华[1] 孙怀君[2] 吴文慧[2] 

机构地区：[1]金华职业技术学院,浙江金华321007 [2]浙江师范大学数理学院,浙江金华321004

出　　处：《沈阳工程学院学报（自然科学版）》2007年第1期83-84,92,共3页Journal of Shenyang Institute of Engineering:Natural Science

基　　金：浙江省金华市科技基金资助项目(2005-1-169)

摘　　要：Fe基纳米非晶丝通过脉冲电流获得Fe基纳米晶丝,可以改善其巨磁阻抗效应.通过在不同的准电流密度下对非晶丝进行退火,并分析退火后Fe基纳米晶丝的巨磁阻抗效应,得出当准电流密度为8.0 V时,可获得最佳的巨磁阻抗效应,其巨磁阻抗效应达到16.911%,退火效果为6.791%.Fe-based nano- crystalline alloy wire can be obtained from Fe- basea amorphous wire oy purse current, it can improve its giant magneto- impedance effect. Annealing amorphous wire under conditions of different current densities, analyzes the giant magneto- impedance effect of Fe- based nano- crystalline alloy wire after anneal,draws the conclusion that when current density is 8.0 V,giant magneto- impedance effect is optimal, is 16. 911%, anneal effect is 6. 791%.

关 键 词：Fe基纳米晶丝 巨磁阻抗效应 脉冲电流 退必 

分 类 号：TG156.2[金属学及工艺—热处理]