尾矿代粘土在干法回转窑水泥生产中的应用研究  

Applied research on utilization of metallic tailings as clay for cement production in dry rotary kiln

作　　者：施正伦[1] 施正展[1] 骆仲泱 焦有宙[1] 周劲松[1] 俞燕平 傅圣勇 岑可法[1] 

机构地区：[1]浙江大学热能工程研究所能源清洁利用国家重点实验室,杭州310027 [2]浙江省诸暨市福利水泥有限公司,诸暨311817

出　　处：《环境科学学报》2007年第2期348-352,共5页Acta Scientiae Circumstantiae

基　　金：国家"十五"科技攻关项目(No.2003BA612A18)~~

摘　　要：为获取尾矿在干法回转窑水泥生产应用的技术参数,在对尾矿和粘土特性进行分析的基础上,在2500t·d-1的新型干法回转窑生产线上进行了浙江诸暨铜尾矿替代粘土配料的应用试验研究.试验采用循序渐进的方法,诸暨铜尾矿按质量分数为1%、2%、3%、5%依次在生产原料中掺配,对试验熟料样品进行了化学成分分析和矿物组成X射线衍射(XRD)分析.试验结果表明,掺铜尾矿生产得到的熟料化学组成和游离氧化钙(f-CaO)含量正常,熟料烧成情况良好;与掺粘土熟料相比,掺铜尾矿熟料矿物组成结构有所调整,早强和高强矿物含量有所增加.熟料物性检测表明,掺铜尾矿生产得到的熟料的各项性能指标均满足技术要求,熟料各龄期强度指标与掺粘土熟料相比略有提高.掺铜尾矿配料与粘土配料主要生产运行指标统计分析表明,试验过程在干法回转窑生产运行稳定的情况下,掺铜尾矿配料较粘土配料,其熟料平均日产量提高10.07%,熟料标煤耗降低8.29%.For obtaining technology parameters of metallic tailings used as clay for cement production in dry rotary kiln, the properties of the metallic tailings and day were analyzed, and applied experiments were performed in a 2500 t ·d^-1 dry rotary kiln by using Zhejiang zhuji copper railings as clay. Metallic tailings were added by gradually increased as 1% , 2% , 3% and 5%, respectively. The ehemical composition of clinker samples was measured and mineral component of clinker samples were quantitatively analyzed by X-ray diffraction. The results revealed that chemical composition and free-CaO content of clinker samples were at normal level. And calcinations of clinker samples were better than clinker samples mixed with clay. The components of the clinker mineral were appreciably adjusted. And the content of earlier and higher compressive strength mineral component increased. The test results of clinker physical performances showed that the indices of clinker all could reach the technology standards. Compared with clinker samples mixed with clay, compressive strength of the cement at different ages was enhanced. Statistic analyses of production indices indicated when copper metallic railings were added, and the producing system was operated well, the average output of clinker per day increased by 10.07% , and the usage of the standard coal decreased by 8.29%.

关 键 词：金属尾矿 粘土 干法回转窑 水泥生产 

分 类 号：X753[环境科学与工程—环境工程]