不锈钢上草绿色钼酸盐转化膜组成的研究  

STUDIES OF THE GRASS-GREEN MOLYBDATE CONVERSION FILM ON STAINLESS STEEL

作　　者：韩克平[1] 方景礼[1] 刘琴[1] 

机构地区：[1]南京大学,应用化学研究所配位化学国家重点实验室,南京经济学院

出　　处：《应用科学学报》1996年第3期353-357,共5页Journal of Applied Sciences

摘　　要：用阴极电沉积法从钼酸盐溶液中获得了草绿色的不锈钢转化膜．该膜具有良好的热稳定性．ＸＰＳ和ＡＥＳ分析表明，膜厚约为１７３ｎｍ．膜的表面钼以Ｍｏ（ＶＩ）存在，而在膜内则以Ｍｏ（ＶＩ）和Ｍｏ（ＩＶ）共存．从ＡＥＳ深度剥蚀曲线的组成恒定区求得膜的组成为：Ｏ５２．８％，Ｍｏ３０．４％，Ｐ１２．５％和Ｆｅ４．３％．循环伏安的氧化峰也证明膜内存在Ｍｏ（ＩＶ）．A grass-green conversion film was formed on stainless steel with the cathodic electcodeposition method from molybdate solution. This film displayed good thermostability. The results of XPS and AES analysis showed that the thickness of the film was 173nm and Mo existed as Mo(VI) on the surface of the film, but as Mo(VI) and Mo(IV) in the niternal layer of the film. The relative atomic percent contents (A.C.%) of the film obtained from the elemental composition constant region of the profile curved by AES were O 52 .8%, Mo 30.4%,P 12.5% and Fe 4.3%respectively. The cyclevoltammetric oxidation peak also showed that the Mo (IV) existed in the internal layer of the film.

关 键 词：彩色膜 钼酸盐 不锈钢 XPS AES 着色法 

分 类 号：TG177[金属学及工艺—金属表面处理]