高强度铜合金表面TiO_2薄膜制备及表征  

Preparation and Characterization of TiO_2 Film on High Strength Copper Alloy

作　　者：徐文清[1] 翟启明[1] 林生岭[1] 谢春生[1] 周虎[1] 

机构地区：[1]江苏科技大学材料科学与工程学院,江苏镇江212003

出　　处：《江苏科技大学学报（自然科学版）》2007年第1期80-84,共5页Journal of Jiangsu University of Science and Technology:Natural Science Edition

摘　　要：利用溶胶-凝胶法在高强度高阻尼CuAlBe合金表面制备TiO2薄膜,并通过扫描电镜、电子能谱、红外光谱、XRD等现代分析手段,对合金表面形貌、成分变化、TiO2的形态、粒子尺寸等进行分析。实验表明:在CuAlBe合金表面涂覆8次、经450℃热处理下能获得致密的连续片状TiO2薄膜;粒子尺寸为50-100 nm,其存在形式主要为锐钛矿型。TiO2 thin films are prepared on the high strength and high damping CuAlBe alloy with sol-gel method by using TiO2 sol solution. The appearance of the surface, the variation of the composition, the form of TiO2 and thesize of the particles are analyzed through SEM ,EDS, Infrared Speeturm and XRD. The results show that the dense continuous mierostrueture of TiO2 withsheet form can be obtained through 8 coating cycles and under 450℃ annealing. The main existing form of TiO2 partieles is anatase with 50 to 100 nanometers.

关 键 词：TIO2薄膜 CUALBE合金 光催化 

分 类 号：TQ13[化学工程—无机化工]