Long-term Performance of Moderate Heat Portland Cement with Double-expansive Sources  

作　　者：叶青 

机构地区：[1]College of Architecture and Civil Engineering, Zhejiang University of Technology

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2007年第1期35-39,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by National Natural Science Foundation of China (No.59493604);Zhejiang Provincial Natural Science Foundation of China (No.597082);China Yangtze River Three Gorges General

摘　　要：The long-term performance of moderate heat Portland cement with double-expansive sources （DE cement） in the system of high MgO clinker and gypsum was studied by XRD, SEM/EDAX and test methods for strength and expansion of cement. Results indicate that the periclase particle, whose size was 5-7.5μm in DE cement clinker containing 4.8 % MgO, existed individually. The periclase hydration in hardened DE cement paste started at about 60 days and completed up to 2 000 days, and ettringite in the paste was stable from 3 days to 2 000 days. Under the conditions of 4.5%-5.0 % MgO in clinker and 2.8%-3.4 %SO3 in cement, ettringite expansion and brucite expansion in DE cement paste had a continuity, entirety and stability. At the ages of 90, 365,730 and 2 000 days the expansion of the paste reached 0.07%-0.11%, 0.16%-0.21%, 0.21%-0.27 %, and 0.29%-0.38%, respectively. The results suggest that by using this cement in mass concrete it may compensate its temperature shrinkage and autogenous shrinkage to some extent.The long-term performance of moderate heat Portland cement with double-expansive sources （DE cement） in the system of high MgO clinker and gypsum was studied by XRD, SEM/EDAX and test methods for strength and expansion of cement. Results indicate that the periclase particle, whose size was 5-7.5μm in DE cement clinker containing 4.8 % MgO, existed individually. The periclase hydration in hardened DE cement paste started at about 60 days and completed up to 2 000 days, and ettringite in the paste was stable from 3 days to 2 000 days. Under the conditions of 4.5%-5.0 % MgO in clinker and 2.8%-3.4 %SO3 in cement, ettringite expansion and brucite expansion in DE cement paste had a continuity, entirety and stability. At the ages of 90, 365,730 and 2 000 days the expansion of the paste reached 0.07%-0.11%, 0.16%-0.21%, 0.21%-0.27 %, and 0.29%-0.38%, respectively. The results suggest that by using this cement in mass concrete it may compensate its temperature shrinkage and autogenous shrinkage to some extent.

关 键 词：BRUCITE ETTRINGITE EXPANSION long-term performance moderate heat Portland cement 

分 类 号：TQ172[化学工程—水泥工业]