钛酸钡陶瓷材料的制备及电磁性能研究  

Synthesis of Barium Titanate and Its Electromagnetic Properties

作　　者：王桂芹[1] 陈晓东[1] 段玉平[1] 李伟平[1] 刘顺华[1] 温斌[1] 

机构地区：[1]大连理工大学材料科学与工程学院,大连116023

出　　处：《无机材料学报》2007年第2期293-297,共5页Journal of Inorganic Materials

基　　金：国家自然科学基金(50402025)

摘　　要：采用溶胶-凝胶法制备出了钛酸钡陶瓷粒子,观察和分析了粒子的成分、形貌和微观结构及其对电磁波的吸收性能,并测定了粉体的复介电常数和磁导率．XRD和TEM分析表明制备的粒子为四方相,粒径在30～40nm左右．制备的钛酸钡／环氧树脂复合吸收材料在8～18GHz范围内对电磁波有良好的吸收效果,当含量为20％时效果最佳．最后针对其吸收特性探讨了钛酸钡粒子的吸收机理．The ceramic marerial of barium titaaate （BT） was synthesized by a sol-gel method. The mircrostructure and morphology of the powders were characterized by IR, XRD and TEM. The dielectric constant and permeability of the mixture of BT powders and paraffin wax were measured. The microwave absorbing performance of BT powder and epoxide （EP） resin composite was studied in the frequency range of 8-18GHz. The results show that the BT powder exists in the form of tetragonal phase with the size in the range of 30-40nm. The BT/EP composite exhibits good microwave absorbing performance in the frequency range of 8-18GHz, when the content of BaTiO3 is 20vo1%, the performance is the best. The microwave absorption mechanism of BaTiO3 powders is mainly due to the dielectric relaxation. The BT powder will be a good candidate for microwave absorbing materials.

关 键 词：陶瓷材料 钛酸钡 电磁性能 吸波机理 

分 类 号：TB332[一般工业技术—材料科学与工程]