室温固化环氧树脂结构胶粘剂的研究  

Study of epoxy resin structure adhesives cured at room temperature with good water resistant

作　　者：丑纪能[1] 邓飞跃[1] 

机构地区：[1]中南大学化学与化工学院,长沙410083

出　　处：《化工新型材料》2007年第3期80-82,共3页New Chemical Materials

摘　　要：制备了室温快速固化综合性能较好的聚氨酯改性环氧树脂结构胶粘剂,探讨了增韧剂,固化剂等因素对胶粘剂力学性能的影响,通过扫描电镜分析了胶粘剂断裂面的形貌特征,研究了胶粘剂形貌特征与力学性能的关系。研究结果表明:聚氨酯增韧环氧树脂既有物理交联产生“强迫互溶”和“协同效应”,又与环氧树脂发生了化学反应,产生的化学键进一步加强了聚合物交联密度和聚合物的强度,当PU预聚体含量为环氧树脂40%时,聚氨酯与环氧树脂形成的互穿网络聚合物互穿程度最大,制备的胶粘剂力学性能最优,室温剪切强度达到20.16MPa。A epoxy resin structure adhesive modified by polyurethane （PU） cured at room temperature was prepared. The effect of the toughening agent,curing agent and other factors to the properties of the adhesive were discussed; The morphology was studied by means of SEM, The relationship between the morphology of the adhesive and the mechanical of the adhesive was also discussed. The results indicated： The interpenetrating polymer network（IPN） based on polyurethane and E51 epoxy resin shown ＂synergism＂ and ＂cooperation effect＇by physical interpenetrating, the desity and intensity of the IPN were further strengthened by the new chemical bond which produced in the curing process. The adhesive have the best mechanical properties when the PU/EP ratio is 40/100,the maximal shear strength of the adhesive is 20. 16 MPa at room temperature.

关 键 词：胶粘剂 环氧树脂 聚氨酯 力学性能 

分 类 号：TQ433.437[化学工程]