氧化铁还原率及金属化率的测量新方法  

A New Method for the Measurement of Degrees of Reduction and Metallization of Iron Oxide

作　　者：郭培民[1] 张殿伟[1] 赵沛[1] 

机构地区：[1]钢铁研究总院先进钢铁流程及材料国家重点实验室,北京100081

出　　处：《光谱学与光谱分析》2007年第4期816-818,共3页Spectroscopy and Spectral Analysis

基　　金：国家自然科学基金项目(50474006)资助

摘　　要：用H2及CO还原氧化铁过程中,使用了X-ray粉末衍射和化学分析方法确定了氧化铁及金属铁的定量分析关系。铁素体(αFe)、奥氏体(γFe)、碳化铁(Fe3C)、磁铁矿(Fe3O4)、赤铁矿(Fe2O3)与浮氏体(Fe0.947O)的摩尔强度定量关系的系数分别为0.56,0.56,0.52,0.87和2.57。通过这些系数,可以计算出氧化铁的金属化率和还原率。Quantitative analyses of mixture composed of iron oxides and metal iron were investigated by means of powder X-ray diffraction and chemical analysis methods for iron oxides reduction by H2 and CO, respectively. The coefficients of quantitative molar intensity ratio of ferrite （αFe）, austenite （γFe）, iron carbide （Fe3 C）, magnetite（Fe3 O4 ） and hematite （ Fe2 O3 ） to wustite （Fe0.947O） are 0. 56, 0. 56, 0.52, 0.87 and 2.57 respectively. The degrees of metallization and reduction of iron oxide were calculated according to these coefficients.

关 键 词：氧化铁 定量分析 X-ray衍射 还原率 金属化率 

分 类 号：TF521.1[冶金工程—钢铁冶金]