柠檬酸络合法制备La_(0.56)Li_(0.33)TiO_3锂离子导电材料  

Preparation of La_(0.56)Li_(0.33)TiO_3 Lithium Ionic Conductor by Citrate Sol-Gel Process

作　　者：李景新[1] 温兆银[1] 许晓雄[1] 顾中华[1] 徐孝和[1] 

机构地区：[1]中国科学院 上海硅酸盐研究所,上海200050

出　　处：《无机材料学报》2007年第3期432-436,共5页Journal of Inorganic Materials

基　　金：国家自然科学基金重点基金(20333040)

摘　　要：采用柠檬酸络合法合成了La2／3-xLi3xTiO3(z=0．11,LLT)复合氧化物材料,通过系统研究影响溶胶和凝胶形成以及粉体晶相结构的各种因素,确定了最佳的合成条件．研究结果表明:柠檬酸络合法所制备的粉体烧结温度降低至1200℃左右,与传统的固相合成法相比具有更高的活性,其烧结温度约降低150℃．烧结所得的陶瓷样品在室温时的晶粒电导和总电导分别达到9×10-4和2．15×10-5S／cm．Superfine powders of La2/3-xLi3xTiO3（x=0.11, LLT） perovskite-type oxides were synthesized by a citrate method. The factors influencing on the formation of sol and gel as well as the crystal structure and morphology of synthesized powders were examined. The effects of sintering temperature on the conductivities of the ceramics were investigated. The results show that the highest electrical conductivity can be obtained for the sample sintered at 1200℃, which is approximately 150℃ lower than that of samples synthesized by the conventional solid state reaction method. The grain and total lithium ion conductivities of the LLT ceramics sintered at 1200℃ are 9 × 10^-4S/cm and 2.15× 10^-5 S/cm at room temperature, respectively.

关 键 词：La2/3-xLi3xTiO3 柠檬酸络合法 锂离子导体 无机电解质 

分 类 号：O646.54[理学—物理化学]