聚合硅酸硫酸铝的絮凝性能及改性研究  

Study of flocculation and modification of polyaluminum silicate sulfate

作　　者：姚剑军[1] 张立武[1] 

机构地区：[1]重庆大学化学化工学院,重庆400044

出　　处：《应用化工》2007年第5期475-477,480,共4页Applied Chemical Industry

摘　　要：以硫酸铝、水玻璃和铝酸钠为原料制备了聚合硅酸硫酸铝(PASS),研究了PASS絮凝性能,并利用聚二甲基二烯丙基氯化铵(PDMDAAC)和聚丙烯酰胺(PAM)对PASS进行复合改性。结果表明,PASS絮凝条件选择为加药量40 mg/L,A l/S i为10-20,原水在pH值6.0-8.0有较好的絮凝效果。在最佳絮凝条件下处理低浊水时,其除浊率达到97%,通过加入少量PDMDAAC对PASS改性后能显著减少PASS用量。A inorganic polymer flocculants polyaluminum silicate sulfate was prepared by using aluminum sulfate,water glass and sodium aluminate as raw materials.The focculating efficiency of PASS was also preliminarily examined by Jar-test.Modification of PASS by using polydimethyl dimly ammonium chloride（PDMDAAC） and polyacrylamide（PASS） was studied.The results showed that PASS has a high floccu-lation performance with the optimum dose of 40 mg/L,Al/Si mole ratio of 10～20 and the pH of water between6.0～8.0,the percentage of removal of turbidity is97% and it can decrease the dose of PASS distinctly when using PDMDAAC as a modifying agent.

关 键 词：聚合硅酸硫酸铝 聚二甲基二烯丙基氯化铵 絮凝剂 

分 类 号：TQ314.253[化学工程—高聚物工业]