硅藻土基轻质多孔陶瓷滤球的研制  

Research and Preparation of Diatomic Porous Ceramics Filtration Media

作　　者：吴建锋[1] 杨学华[1] 徐晓虹[1] 郭全胜[1] 

机构地区：[1]武汉理工大学材料科学与工程学院,武汉430070

出　　处：《武汉理工大学学报》2007年第5期17-19,共3页Journal of Wuhan University of Technology

基　　金：山东铝业公司资助(2004002)

摘　　要：以硅藻土为基料,加入天然有机细粉为造孔剂,同时加入适量的其它添加剂,采用成球机成型工艺,制备了性能优良的硅藻土基多孔陶瓷。随着造孔剂的加入量、烧成制度的改变,气孔率从53%增加至72%,密度从1.3 g/cm3到0.7 g/cm3改变,压碎强度则从13.0 MPa降至6.8 MPa。另外,探讨了白云石作为成孔剂能显著提高多孔陶瓷性能的机理。Diatomite porous ceramics of good quality were made from diatomite, some other additives and pore-forming agent by bailing machine in this experiment. With the change of the amount of pore-forming agent and firing schedule, the main characters of the porous ceramics are change as follow： porosity from 53% to 72%, density from 1.3 g/cm^3 to 0.78 g/cm^3, and compressive strength from 13 MPa to 6.8 MPa. Further more, the reason that dolomite could improve the performance of porous ceramics was discussed.

关 键 词：硅藻土 多孔陶瓷滤球 成球机成球 造孔剂 性能 

分 类 号：TQ174.79[化学工程—陶瓷工业]