Influence of Ni-electrodeposited Pretreatment on Galvanized Coatings of Reactive Steels  

作　　者：车淳山 

机构地区：[1]College of Materials Science and Engineering,South China University of Technology

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2007年第2期221-224,共4页武汉理工大学学报（材料科学英文版）

摘　　要：Four types of steel sheets containing 0.04%, 0.09%, 0. 14% and 0.36% Si, respectively, were electrodeposited with a nickel layer of 3 tam in thickness and then galvanized in molten Zn at 450℃ for various periods of time. The formation and growth of intermetallic compound layers on the surface of the samples were investigated by SEM and EDS. The experimental results show that the method of Ni-electrodeposited pretreatment can distinctively restrain the over-growth of the galvanized coatings of reactive steels and get eligible coatings with a proper thickness, bright appearance and strong adherence. EDS results indicate that a series of Ni-Zn intermetallic compounds γ′, γ and δ, are first formed on the surface of the samples. With a prolonged immersion time, the F2-Fe-Zn-Ni and δ-Fe-Zn are formed accompanied by the gradual disappearance of γ′, γ and δ2 layer. After a longer immersion time, the lumpy ζ- Fe-Zn occurs between δ and liquid Zn and the F-Fe-Zn does between steel substrate and δ. Subsequently, ζ is in the form of a continuous and compact layer. The method of Ni-electrodeposited pretreatment changes the formation of Fe-Zn intermetallic compounds, which delay the growth of lumpy （and promote the growth of compact δ. Consequently, the abnormal growth of reactive steels is eliminated.Four types of steel sheets containing 0.04%, 0.09%, 0. 14% and 0.36% Si, respectively, were electrodeposited with a nickel layer of 3 tam in thickness and then galvanized in molten Zn at 450℃ for various periods of time. The formation and growth of intermetallic compound layers on the surface of the samples were investigated by SEM and EDS. The experimental results show that the method of Ni-electrodeposited pretreatment can distinctively restrain the over-growth of the galvanized coatings of reactive steels and get eligible coatings with a proper thickness, bright appearance and strong adherence. EDS results indicate that a series of Ni-Zn intermetallic compounds γ′, γ and δ, are first formed on the surface of the samples. With a prolonged immersion time, the F2-Fe-Zn-Ni and δ-Fe-Zn are formed accompanied by the gradual disappearance of γ′, γ and δ2 layer. After a longer immersion time, the lumpy ζ- Fe-Zn occurs between δ and liquid Zn and the F-Fe-Zn does between steel substrate and δ. Subsequently, ζ is in the form of a continuous and compact layer. The method of Ni-electrodeposited pretreatment changes the formation of Fe-Zn intermetallic compounds, which delay the growth of lumpy （and promote the growth of compact δ. Consequently, the abnormal growth of reactive steels is eliminated.

关 键 词：hot-dip galvanizing electrodepositing Ni reactive steel intermetallic compound 

分 类 号：TG174.44[金属学及工艺—金属表面处理]