苏柳799、苏柳172制强韧硫酸盐浆的研究  

Kraft pulping of Salix × jiangsuensis CL ‘J799’ and CL ‘J172’

作　　者：房桂干[1] 潘明建[2] 

机构地区：[1]中国林业科学研究院林产化学工业研究所 [2]江苏省林业科学研究所

出　　处：《江苏林业科技》1997年第1期27-30,34,共5页Journal of Jiangsu Forestry Science & Technology

基　　金：林业部"八五"重点研究项目

摘　　要：运用典型硫酸盐法制浆工艺对速生人工林苏柳１７２、苏柳７９９（Ｓａｌｉｘ×ｊｉａｎｇｓｕｅｎｓｉｓＣＬ．‘Ｊ１７２’ａｎｄＣＬ．‘Ｊ７９９’）制强韧硫酸盐浆性能进行了系统研究，活性碱用量为１０％～１６％，硫化度２５％，液比１∶４，升温７５ｍｉｎ至１７０℃保温１２０ｍｉｎ，研究结果表明，两种试材用碱量均低，在蒸煮至Ｋａｐｐａ值２０左右时，Ｊ１７２，活性碱用量约为１３．１％（Ｎａ２Ｏ计），Ｊ７９９活性碱用量约为１３．８％。细浆得率高达５２％～５３％（对绝干木片），纸浆性能研究结果表明，纸浆易于打浆，成纸性能优良，有很优秀的强度性能，在３０°ＳＲ左右时，裂断长８．２～８．６ｋｍ，耐破度达５．５～６．４ｋＰａ·ｍ２／ｇ，撕裂指数达６．１～９．７ｍＮ·ｍ２／ｇ，撕折度７５０次以上，Ｊ１７２，Ｊ７９９皆为制强韧硫酸盐浆良好原料，可以用于生产强韧包装纸板，高档牛皮卡纸，经漂白后可以用于部分替代进口长纤维配抄高级文化、印刷用纸。The paper was prepared to report our investigations on Salix × jiangsuensis CL ‘J799’ and CL ‘J172’ wood samples from rapid growing plantations, by means of a typical kraft pulping process with the followed conditions: active alkali usage range of 10%～ 16%,sulfidity 25%,wood to liquor ratio 1∶4, time to temperature 75 min,and time at temperture 120 min.The results show that, at the kappa no. 20, both of the two clones consumed lower alkali chemicals, i.e. about 13 1%(as Na 2O) for J172,13 8%(as Na 2O) for J799. The pulp yields were up to 52%～53%(on o.d.wood). Kraft pulps from above species were easy to be beaten and good of paper making and strength properties. At the drainability level of 30 0 SR, handsheets were made from both J172 and J799 pupls and physical properties were tested at the GB standard conditions. The results shows that breaking length was at range of 8 2～8 6km, burst indices of 5 5～6 4 kPa.m 2/g, tear indices of 6 1～9 7 mN·m 2/g and fold endurance of more than 750.Therefore, salix×jiangsuensis CL ‘J799’ and CL ‘172’ would be of good potential species for pulwood plantations, their kraft pulps could be used as furnishes for various grades of liner board, high strength packaging paper products etc. By a suitable bleaching process, their bleached pulps also could be used to produce good quality writing, printing and packaging paper grades.

关 键 词：苏柳 强韧硫酸盐法 制浆工艺 

分 类 号：TS743[轻工技术与工程—制浆造纸工程]