321/Qd370qD爆炸焊接界面附近非晶相  

Amorphous Phases Beside Interface in 321/Qd370qD Explosive Welded Plate

作　　者：张金民[1] 岳宗洪[1] 韩顺昌[1] 文九巴[2] 张天佑[1] 魏保恒[1] 许庆合[1] 

机构地区：[1]洛阳船舶材料研究所,河南洛阳471039 [2]河南科技大学材料科学与工程学院,河南洛阳471003

出　　处：《热加工工艺》2007年第11期12-13,共2页Hot Working Technology

摘　　要：利用透射电子显微镜研究了321/Qd370qD爆炸焊接界面附近基板内的组织。结果表明,基板珠光体内部存在大量的弥散分布的非晶相。探讨了非晶相的形成原因,认为非晶相可能是由爆炸产生的高压应力形成的。Microstructures beside the welding interface in 321/Qd370qD explosive .welded plate were studied by transmission electron microscopy （TEM）, The results show that there are a lot of amorphous phases in perlite, Its formation cause is considered that the amorphous phases may be formed by high pressure stress.

关 键 词：爆炸焊接 非晶 高压 

分 类 号：TG456.6[金属学及工艺—焊接]