合金球墨铸铁初轧辊热处理工艺  

Heat Treatment Process of Alloy Nodular Cast Iron Bloom Rollers

作　　者：齐增生[1] 梁谨 安会芬[3] 

机构地区：[1]邢台职业技术学院机电系,河北邢台054035 [2]邢台轧辊(集团)有限公司,河北邢台054025 [3]河北机电职业技术学院,河北邢台054000

出　　处：《金属热处理》2007年第6期99-101,共3页Heat Treatment of Metals

摘　　要：对合金球墨铸铁初轧辊的化学成分和热处理工艺进行了试验研究,提出了最佳热处理工艺。结果表明,喷雾淬火可以有效减少或消除铸态组织中的牛眼状铁素体,提高轧辊的综合力学性能。经过880-920℃加热喷雾淬火、吹风续冷,540-580℃回火后,辊身工作层组织为球状石墨＋回火索氏体和少量碳化物,抗拉强度〉700MPa,硬度为42-48 HS。The chemical composition and heat treatment process of alloy nodular cast iron bloom rollers were expenmentauy studied. The optimum heat treatment parameters were put forward. The results show that the spray quenching is able to decrease or eliminate the ox-eyes like ferrite in cast microstructure,and improve the comprehensive mechanical properties of the rolls. After being heated at 880 -920 ℃, and then spray quenched ,following air-cooled and at last tempering at 540 580 ℃ ,the microstructure of nodular graphite,tempering sorbite and a little of cementite formed in the surface working zone of the rolls. The tensile strength of the working zone is more than 700 MPa and the hardness was 42 -48 HS.

关 键 词：初轧辊 合金球墨铸铁 热处理工艺 

分 类 号：TG143.8[一般工业技术—材料科学与工程] TG156[金属学及工艺—金属材料]