攀钢120t转炉-LF+RH流程20CrMnTiH窄淬透性带齿轮钢的试制  

Pilot Production of Narrow Hardenability Band Gear Steel 20CrMnTiH by 120 t Converter-LF+RH Process at Panzhihua Steel

作　　者：蒲学坤[1] 柯晓涛[2] 邓通武[2] 

机构地区：[1]昆明理工大学,昆明650093 [2]攀枝花钢铁研究院,攀枝花617000

出　　处：《特殊钢》2007年第4期50-51,共2页Special Steel

摘　　要：攀钢采用120 t转炉-130 t LF+RH-280 mm×380 mm方坯连铸-热轧工艺生产Φ25～160 mm 20CrMnTiH齿轮钢(%:0.20～0.22C、0.25～0.31Si、0,93～1.00Mn、1.03～1.15Cr、0.05～0.08Ti)。检验结果表明,钢中氧含量(10～20)×10^(-6)(平均14×10^(-6)),淬透性(J_9,J_(15))带宽△HRC值≤7,机械性能和组织均符合GB/ T5216-2004标准要求。The φ25 - 160 mm round bars of gear steel 20CrMnTiH- 0.20 - 0.22C, 0.25 - 0.31Si, 0.93 - 1.00Mn, 1.03 - 1.15Cr, 0. 05 - 0. 08Ti were pilot- produced by 120 t converter - 130 t LF ＋ RH - 280 mm × 380 mm bloom concasting - hot rolling process at Panzhihua Steel. The examination results showed that oxygen content in steel was （ 10 - 20） × 10^-6 （ average 14 × 10^-6 ）, hardenability （ J9, J15 ） band width - △HRC value ≤7 ; mechanical and structure all met the requirement of standard GB/T5216-2004.

关 键 词：20CRMNTIH齿轮钢 转炉 LF+RH 

分 类 号：TF713[冶金工程—钢铁冶金] TF777.2[金属学及工艺—金属压力加工] TG335.11