梯度GF／SAN复合材料的制备  

Preparation of Gradient GF/SAN Composite

作　　者：陈大为[1] 翟林峰[1] 杨华忠[1] 史铁钧[1] 

机构地区：[1]合肥工业大学化工学院,安徽合肥230009

出　　处：《现代塑料加工应用》2007年第3期23-26,共4页Modern Plastics Processing and Applications

基　　金：该课题属于国家自然科学基金赞助项目(基金代码50373010)。

摘　　要：酸性条件下,使用强氧化剂、正硅酸乙酯(TEOS)和苯基三乙氧基硅烷(PTES)依次对短玻璃纤维(GF)表面进行改性,制备了梯度GF／苯乙烯-丙烯腈共聚物(SAN)复合材料,利用光学显微镜和红外光谱(FTIR)对梯度GF和普通GF进行了对比分析。结果表明,改性后的GF表面形成了由无机相向有机相逐渐过渡的梯度结构,GF／SAN复合材料冲击强度测试和断面的场发射扫描电镜(FESEM)分析表明梯度GF与SAN树脂具有很好的相容性和更好的冲击性能。Gradient GF/SAN composites were obtained by treating short glass fibers with strong oxidants, TEOS and PTES in acid solution respectively. Modified glass fibers and short glass fibers were analyzed by optics microscope and FTIR. The results indicate that there is gradient structure changing gradually from inorganic phase to organic phase on the surface of gradient glass fibers. The impact strength test of GF/SAN composite and impact fracture photos （FESEM） show that the gradient GF/SAN composite has better compatibility and impact strength.

关 键 词：正硅酸乙醋 梯度玻璃纤维 苯乙烯-丙烯庸共聚物 制备 

分 类 号：TB332[一般工业技术—材料科学与工程]