阳极对YSZ薄膜SOFC性能的影响  

Effect of anodes on the performance of YSZ thin film SOFC

作　　者：陈孔发[1] 吕喆[1] 艾娜[1] 苏文辉[1] 

机构地区：[1]哈尔滨工业大学物理系,黑龙江哈尔滨150001

出　　处：《电池》2007年第2期143-144,共2页Battery Bimonthly

摘　　要：研究了两种阳极对YSZ薄膜固体氧化物燃料电池(SOFC)性能的影响。NiO-YSZ阳极和NiO-SDC-YSZ阳极支撑的YSZ薄膜电池,在800℃时的开路电压分别为1.09 V和0.87 V,最大功率密度分别为0.86 W/cm2和0.16 W/cm2。NiO-SDC-YSZ阳极电池的电极总阻抗比NiO-YSZ阳极电池的高出58%。The effects of two kinds of anodes on the performance of YSZ thin film solid oxide fuel cell （SOFC） were studied. The YSZ films cells fabricated on NiO-YSZ anode and NiO-SDC-YSZ anode produced open-circuit voltage of 1.09 V and 0.87 V and the maximum power density of 0.86 W/cm^2 and 0.16 W/cm^2 at 800 ℃, respectively. The total electrode resistance of the ceU with NiO-SDC-YSZ anode was 58% higher than that of the cell with NiO-YSZ anode.

关 键 词：NiO-YSZ阳极 NiO-SDC-YSZ阳极 SOFC 浆料旋涂法 YSZ薄膜 