酚醛环氧／双酚A二(二苯基)磷酸酯／有机蒙脱土阻燃ABS Ⅲ．冲击改性剂对阻燃ABS性能的影响  

NE/BDP/OMMT Flame Retarded ABSⅢ. Effect of Impact Modifier on Property of Flame Retarded ABS

作　　者：林晓丹[1] 徐忠英[1] 曾幸荣[1] 徐迎宾 

机构地区：[1]广州华南理工大学材料学院,广东广州510640 [2]广州花都科苑企业有限公司,广东广州510860

出　　处：《塑料工业》2007年第B06期263-264,271,共3页China Plastics Industry

摘　　要：选用SBS和ABS高胶粉对酚醛环氧树脂(NE)、NE/有机蒙脱土(OMMT)纳米复合物与双酚A二(二苯基)磷酸酯(BDP)以及硅烷偶联剂和硼酸锌(ZB)复配制备的无卤阻燃ABS进行增韧改性。发现ABS高胶粉增韧效果比SBS好,冲击断面呈现韧性断裂,且对氧指数和拉伸强度影响较小。Halogen-free flame retardant ABS was prepared by using novolac epoxy （NE）, NE/organophilic montmorillonite （OMMT）, bisphenol A bis （diphenyl phosphate） （BDP）, coupling agent and zinc borate （ZB） as flame retardants. It was found the property of ABS toughened with high robber content was better than that of ABS toughened with SBS; the fracture surface of the ABS toughened with rubber was of ductile fracture, and the effect of rubber on LOI and tensile strength of the toughened ABS was little.

关 键 词：ABS高胶粉 SBS 增韧 冲击强度 阻燃 