粉末冶金Ti-6Al-4V固溶时效热处理工艺研究  

Study of solution and aging processing of Ti-6Al-4V PM alloy

作　　者：郭训忠[1] 黎俊初[1] 张国光[1] 熊洪淼[1] 闵嗣林[1] 

机构地区：[1]南昌航空工业学院,江西南昌330063

出　　处：《南昌航空工业学院学报》2007年第1期35-39,共5页Journal of Nanchang Institute of Aeronautical Technology（Natural Science Edition）

摘　　要：对采用热等静压工艺制备的粉末Ti-6Al-4V合金的固溶时效热处理工艺进行了研究,探讨了不同的固溶温度、时效温度及时效时间对该合金材料力学性能的影响。结果表明,当固溶时效工艺为935℃+36min+水淬、470℃+6h+空冷时,该合金材料的综合力学性能较佳,这说明固溶时效热处理参数的合理选择对于进一步地提高Ti-6Al-4V粉末冶金件的力学性能起着重要作用。A study on parameters of solution and aging processing of PM Ti-6Al-4V which were prepared by HIP processing was presented. Meanwhile, the influences of different solution temperature, aging temperature and aging time on mechanical properties of PM Ti-6Al-4V were investigated. The results show that the mechanical properties of ruaterials are most preferential when solution and aging processing is 935℃ ＋ 36min ＋ WQ,470℃ ＋ 6h ＋ AC. It indicates that rational choices of parameters of solution and aging processing play important role in file further improvement of mechanical properties of PM Ti-6Al-4V.

关 键 词：TI-6AL-4V合金 固溶时效 粉末冶金 热等静压 力学性能 

分 类 号：TG166.5[金属学及工艺—热处理]