氧化锰对含硫铝酸钙矿物硅酸盐水泥烧成的影响  

Effect of Manganese Dioxide on Burning of Clinkering of Cement Containing C4A3 Mineral

作　　者：陈琳[1] 沈晓冬[1] 马素花[1] 黄叶平[1] 钟白茜[1] 

机构地区：[1]南京工业大学材料科学与工程学院,南京210009

出　　处：《硅酸盐通报》2007年第3期529-532,546,共5页Bulletin of the Chinese Ceramic Society

基　　金：国家"973"计划重点基础研究(2001CB610701);江苏省"六大人才高峰"资助项目

摘　　要：研究了MnO2对含硫铝酸钙矿物硅酸盐水泥熟料的易烧性及矿物形成的影响。借助化学分析测定了水泥熟料中游离氧化钙(f-CaO)的含量,用差热分析(DSC)研究了矿物形成过程,采用X射线衍射(XRD)分析了熟料矿物成分。结果表明:生料中掺入少量的MnO2能改善水泥生料的易烧性,促进f-CaO的吸收,并且利于硫铝酸钙(C4A3-S)与硅酸三钙(C3S)在低温下共存。The effect of manganese dioxide on the bumability and mineral formation of the clinker containing C4A3S was investigated. The f-CaO content, mineral composite and formation of mineral in the clinker were analyzed respectively by chemical analysis, differential scanning calorimetry （DSC） and Xray diffraction （XRD）. The results show that adding minor amount of MnO2 into the raw material can improve the burnability of raw material, promote the f-CaO absorption and benefit the coexistence between calcium sulphoaluminate （C4A3S） and tricalcium （C3S）.

关 键 词：氧化锰 硫铝酸钙 硅酸盐水泥 

分 类 号：TQ172[化学工程—水泥工业]