Citric Gel Synthesis and Luminescent Properties of Ce^(3+)-Activated SrGa_2O_4 Phosphor  

Citric Gel Synthesis and Luminescent Properties of Ce^(3+)-Activated SrGa_2O_4 Phosphor

在线阅读下载全文

作  者:乔彬 唐子龙 张中太 陈雷 

机构地区:[1]State Key Laboratory of New Ceramics and Fine Processing,Department of Materials Science and Engineering,Tsinghua University

出  处:《Journal of Rare Earths》2007年第3期286-290,共5页稀土学报(英文版)

基  金:Project supported by the National Natural Science Foundation of China(59872016)

摘  要:Ce^3+-activated SrGa2O4 phosphor was synthesized by a method of citric gel,wherein citric acid served as a chelate agent,and the as-synthesized powder was calcined in a slightly reduced ambient.The crystallization characteristics of the sample varied with the calcining temperature.Compared with the phosphor prepared by the solid-state reaction,the phosphor synthesized by citric gel was calcined at a relatively lower temperature.Consequently,the volatilization of Ga2O3 during high-temperature calcining process was avoided.The typical double-peak emission of Ce^3+ originated from 2D(5d)→4F5/2(4f),and 2D(5d)→4F7/2(4f)was observed,and the intrinsic emission of SrGa2O4 host was much restricted.The emission intensity varied with the calcining temperature because the different crystallinity and the optimal concentration of Ce-dopant was determined at 3%.Ce^3+-activated SrGa2O4 phosphor was synthesized by a method of citric gel,wherein citric acid served as a chelate agent,and the as-synthesized powder was calcined in a slightly reduced ambient.The crystallization characteristics of the sample varied with the calcining temperature.Compared with the phosphor prepared by the solid-state reaction,the phosphor synthesized by citric gel was calcined at a relatively lower temperature.Consequently,the volatilization of Ga2O3 during high-temperature calcining process was avoided.The typical double-peak emission of Ce^3+ originated from 2D(5d)→4F5/2(4f),and 2D(5d)→4F7/2(4f)was observed,and the intrinsic emission of SrGa2O4 host was much restricted.The emission intensity varied with the calcining temperature because the different crystallinity and the optimal concentration of Ce-dopant was determined at 3%.

关 键 词:citric gel luminescence strontium gallate rare earths 

分 类 号:O614.33[理学—无机化学]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象