Serirez AP-ZF在免烫整理中的应用  

Application of Serirez AP-ZF to DP finishing

作　　者：李峥嵘[1] 许松华 Gary Nicholson Martin 刘燕浓 傅科杰[3] 代云刚 

机构地区：[1]东华大学化学与化工学院生态纺织教育部重点实验室,上海200051 [2]约克夏(亚太)有限公司,广东广州510660 [3]宁波出入境检验检疫局纺织品中心,浙江宁波315012

出　　处：《印染》2007年第14期25-27,共3页China Dyeing and Finishing

摘　　要：采用Serirez AP-ZF水溶性低分子改性聚合物进行全棉织物免烫整理,既能提高织物的抗皱性,又能保证整理织物强力和降低缩水率,且不会释放出游离甲醛。通过分析焙烘温度、树脂用量等因素对织物强力和平整度的影响,确定了最优化的免烫整理工艺,即：Serirez AP-ZF140-160g/L;催化剂MC35-40g/L;有机硅柔软剂20g/L;整理液pH值5左右;100℃预烘3min;160°-170°焙烘1min。During wash and wear finish of pure cotton fabric, the water soluble low molecule modified polymer Serirez AP-ZF was used to increase the crease resistance, ensure the strength and reduce the water shrinkage of finished fabric without free formaldehyde. The influence of baking temperature and dosage of resin on strength and levelness of the fabric were analysed. Based on trials,the optimal process of wash and wear finish was defined, that is, Serirez AP-ZF 140 - 160 g/L, catalyst MC 35 -40 g/L, organic silicon softener 20 g/L, pH value about 5, pre-drying at 100 ℃ for 3 min;baking at 160- 170 ℃ for 1 min.

关 键 词：耐久压烫整理 改性聚合物 棉织物 

分 类 号：TS195.55[轻工技术与工程—纺织化学与染整工程]