电磁振动雾化-速凝镁粉钝化表征研究  

Passivation Characteristics of Magnesium Powder Prepared by Electromagnetic Vibration Atomizing and Quenching

作　　者：梁乃茹[1] 赵军[1] 黄继民[1] 解萍[1] 

机构地区：[1]包头稀土研究院

出　　处：《特种铸造及有色合金》2007年第7期502-503,共2页Special Casting & Nonferrous Alloys

基　　金：内蒙古自治区自然科学基金资助项目(200508010711)

摘　　要：用电磁振动雾化-速凝法制备了粒度为0·2～1·0mm的镁粉,研究了这种速凝镁粉在1000℃的阻燃时间。结果表明,速凝镁粉阻燃时间为17～21s,而铣削-钝化镁粉阻燃时间为11～14s。扫描电镜和能谱仪观察和分析发现,速凝镁粉存在表面碳富集,迅速凝固产生的致密表面,增强了粉粒表面的化学稳定性,产生了钝化效果。The ignition-proof time of the magnesium powder with 0.2～1.0 mm in size prepared by electromagnetic vibration atomizing and quenching has been examined at 1 000 ℃.The results show that the ignition-proof time of rapidly-solidified magnesium powder keeps for 17～21s while that of milling-passivated magnesium powder keeps for 11～14 s.The morphology of the rapidly-solidified magnesium powder was observed by SEM and EPMA.It is found that the C-enrichment on the surface of the magnesium powder can be observed.The chemical stability of powder surface can be strengthened to lead to the passivation effects due to the formation of compact surface during rapid solidification.

关 键 词：电磁振动雾化 速凝 镁粉 钝化 

分 类 号：TB44[一般工业技术]