Preparation of Crack-free 3Y-TZP/Al_2O_3 Composite Ceramic Fiber by Electrolysis-sol-gel Method  

作　　者：LI Jian-jun JIAO Xiu-ling CHEN Dai-rong 

机构地区：[1]Department of Chemistry Shandong University, Jinan 250100, P. R. China

出　　处：《Chemical Research in Chinese Universities》2007年第4期377-380,共4页高等学校化学研究（英文版）

基　　金：Supported by National High Technology Research and Development Program of China(No.2002AA2040).

摘　　要：Polycrystalline 3Y-TZP/Al2O3 tetragonal zirconia fiber was obtained by the pyrolysis of gel fibers using zirconium oxychloride octahydrate（ZOC） as the raw material. The spinnable zirconia sol was prepared by electrolyzing the zirco-nium oxychloride octahydrate（ZOC） solution in the presence of acetic acid and sugar（ sucrose, glucrose or fructose） , in which the molar ratios of CH3 COOH/ZOC and sugar/ZOC were 1.0-4.0 and 0.2-0.4, respectively. The pre- pared tetragonal zireonia fibers sintered at different temperatures showed smooth and crack-free surfaces with diame, ters of 5-10 μm. The addition of Al2O3 enhanced the sintering process and prevented the crystals from growing. Thermogravimetric analysis（TG）, X-ray diffraction （ XRD ）, Fourier transform infrared spectroscopy（FTIR）, and scanning electron microscope（SEM） techniques were used to characterize the prepared fibers.Polycrystalline 3Y-TZP/Al2O3 tetragonal zirconia fiber was obtained by the pyrolysis of gel fibers using zirconium oxychloride octahydrate（ZOC） as the raw material. The spinnable zirconia sol was prepared by electrolyzing the zirco-nium oxychloride octahydrate（ZOC） solution in the presence of acetic acid and sugar（ sucrose, glucrose or fructose） , in which the molar ratios of CH3 COOH/ZOC and sugar/ZOC were 1.0-4.0 and 0.2-0.4, respectively. The pre- pared tetragonal zireonia fibers sintered at different temperatures showed smooth and crack-free surfaces with diame, ters of 5-10 μm. The addition of Al2O3 enhanced the sintering process and prevented the crystals from growing. Thermogravimetric analysis（TG）, X-ray diffraction （ XRD ）, Fourier transform infrared spectroscopy（FTIR）, and scanning electron microscope（SEM） techniques were used to characterize the prepared fibers.

关 键 词：ELECTROLYSIS Sol-gel ZIRCONIA Ceramic fiber Al2O3 