时效态Cu-Cr-Zr-Mg-RE合金的组织与性能  被引量:22

Microstructure and properties of aging Cu-Cr-Zr-Mg-RE alloy

在线阅读下载全文

作  者:慕思国[1] 曹兴民[2] 汤玉琼[2] 向朝建[2] 杨春秀[2] 郭富安[2] 唐谟堂[1] 

机构地区:[1]中南大学冶金科学与工程学院,长沙410083 [2]苏州有色金属加工研究院,苏州215026

出  处:《中国有色金属学报》2007年第7期1112-1118,共7页The Chinese Journal of Nonferrous Metals

基  金:中国铝业科技资助项目(2005KJA09)

摘  要:采用高分辨电子显微镜(HRTEM)和光学显微镜(OM)研究Cu-0.43%Cr-0.17%Zr-0.05%Mg-0.05%RE(质量分数)合金的微观组织,测试不同时效工艺下合金的抗拉强度和电导率等性能。结果表明:合金经过冷轧后,在450℃时效4 h,析出相细小且弥散分布在基体中,合金具有较好的综合性能。HRTEM和能谱分析表明,铬相在合金中有棒状、六边形和球状3种存在形态;锆主要以富锆相存在于合金基体中;合金在400℃时效时,观察到了亚稳相CrCu2(Zr,Mg)及其分解过程。The microstructure of Cu-0.43%Cr-0.17%Zr-0.05%Mg-0.05%RE (mass fraction) alloy was studied by high resolution transmission electron microscopy and optical microscopy. The electrical conductivity, tensile strength and micro-hardness of this alloy after cold rolling and aging treatment were investigated. The results show that the alloy aged at 450℃ for 4 h has good combination of physical and mechanical properties. The analyses of HRTEM show that three kinds of chromium-rich phase, such as club-shaped, hexagonal shape and spherical shape exist in the alloy. The zirconium-rich phase and decomposing CrCu2(Zr, Mg) phase are observed at aging temperature of 400℃.

关 键 词:Cu-Cr-Zr-Mg-RE合金 微观组织 电导率 抗拉强度 

分 类 号:TD98[矿业工程—选矿]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象